Marinite P, Marinite I & Marinite M

Oven dried formulations of BNZ boards are used in a variety of heat insulating processes, fire protection and machined parts. Selection is commonly based on a balance between strength and insulating qualities. Examples include oven walls and linings, soldering insulation, fire doors, fire training burn buildings, cable trays, personnel protection, and as USCG-approved insulation for marine ships and off-shore rigs. Back-up insulation applications include ladles, torpedo cars and tundishes in the iron and steel industry, lime and cement plant rotary kilns, and aluminum die cast holding furnaces.

 

Properties  
  MARINITE TRANSITE
Aluminum Contact Boards  
  A C        
High Temperature Structural Insulation  
CS85     P I&M    
Low Temperature Industrial Board  
          HT 1000
Available thicknesses   1⁄4″ – 3″ 1⁄2″ – 3″ 1″ – 2″ 1⁄2″ – 2″ 1⁄2″ – 3″ 1⁄4″ – 3″ 1⁄2″ – 3″
Sheet Sizes       ALL SHEETS ARE 4 ft. x 8 ft.    
Density                
    pcf   85 65 54 60 46 100 98
    (kg/m)   (1362)  (1041) (865) (961) (737) (1602) (1570)
Modulus of Rupture (Flexural strength)
   
psi
   kg/cm²
  3000
(210)
1400
(98) 
900
(63)
1400
(98)
800
(56)
2600
(183)
3000
(211)
Comprehensive Strength %              
    Ultimate Load,            psi   10300 3000 2200 10,400 13,350
                                    kg/cm²   (724)  (211) (155) (731) (939)
    @ 5% Deformation,    psi   6400 2400 1600 3050 1000 6500
                                    kg/cm²   (450)   (169) (112) (214) (70) (457)
Moisture Content %              
    (normal), % of dry weight   1.0 2.5 2.5 3.0 3.0 12 7
Thermal Conductivity                
    Mean temperature, Btu-in/ft², hr, °F                
     250°F   2.40 2.40
      400°F   2.13 –   .99 1.13 0.81
      600°F   –   1.00  1.15 0.79
      800°F   1.94 1.92 1.03  1.16 0.81
      1000°F   2.01 1.95 1.06 1.17 0.86
   Mean temperature, (W/mk)                
      121°C   0.34 0.34
      204°C   0.31  0.14  0.16 0.12
      316°C   0.14  0.17 0.11
      427°C   0.28  0.28 0.15 0.17 0.12
      538°C   0.29 0.28 0.15  0.17 0.12
Shrinkage                
  24 hrs @   1600°F 1350°F 1350°F 1200°F 1200°F 600°F 600°F
    Linear (Length or width), %   0.24 0.1 2.3 0.6  0.4 0.85 0.14
    Thickness, %   2.0 0.8 9.4 2.1 1.4 3.7 0.41
Electrical                        
Arc Resistance, seconds, ASTM D 495   304 260 272
Volume Resistivity, ohm-cm, ASTM D 257   4.52 x 1012     5.0 x 108 9.8 x 107 7.1 x 1010 1.25 x 1013
Dielectric Strength, v/mil, ASTM D 495   61 46 45 35 56
Screw Holding Strength                          
   @ 7⁄8″ penetration, lbs   875 240 220 500 200
                               (k/g)   (397) (109) (100) (227) (91)

Note: All BNZ products are non-asbestos.
         Test results represent typical average values obtained in accordance with accepted test methods.