Typical Data STANDARD ASTM C 155 GRADES
Properties BNZ-20 BNZ-23 BNZ-23 HS BNZ-23A BNZ-26 BNZ-26-60 BNZ-28 BNZ-3000 BNZ-32
ASTM Classification 20/23 23 23 23 26 26 28 30 32
Temperature Use Limit
(Normal oxidizing atmosphere)
°F
°
C
2300
1260
2300
1260
2300
1260
2300
1260
2600
1427
2600
1427
2800
1538
3000
1649
3200
1760
Density, Avg.
nbsp;   ASTM C 134
lb/ft³
kg/m³
lb/BEq
kg/str.
36
577
2.1
0.9
37
593
2.2
1.0
42
673
2.5
1.1
33
529
1.93
0.86
48
769
2.8
1.3
50
801
2.9
1.3
55
881
3.2
1.5
65
1041
3.8
1.7
75
1201
4.4
2.0
Modulus of Rupture
ASTM C 133
lb/in²
MPa
kg/cm²
95
0.7
6.7
105
0.7
7.4
140
1.0
9.9
115
0.79
8
200
1.4
14.1
190
1.3
13.4
220
1.5
15.5
250
1.7
17.6
300
2.1
21.1
Cold Crushing of Strength
ASTM C 133
lb/in²
MPa
kg/cm²
105
0.7
7.4
125
0.9
8.8
190
1.3
13.4
145
1
10.2
270
1.9
19.0
290
2.0
20.4
340
2.3
23.9
440
3.0
31.0
450
3.1
31.7
Permanent Linear Change %
    ASTM C 210
    24 hrs at soaking
temp: °F (°C)
    2250 (1232) 0.0 0.0 0.0 0.0
    2350 (1290)
    2450 (1343)
    2550 (1399) -0.4 -0.2
    2750 (1510) -0.7
    2800 (1538)
    2950 (1621) -0.7
    3150 (1732) -0.4
Reversible Linear Thermal Expansion %
    at 2000°F (1093°C) 0.6 0.6 0.6 0.6 0.6 0.6 0.65 0.65 0.65
Hot Load Strength %
    ASTM C 16 deformation
    10 psi load for 11/2 hours: °F (°C)
    2000 (1093) 0 0 0 0
    2200 (1204) 0.2 0.1 0.1
    2400 (1316) 0.3 0.2
Thermal Conductivity Btu-in/ft², hr, °F
    ASTM C 182 (W/mk)
    Mean temperature, °F (°C)
      500 0.9 1.0 1.2 .92 1.6 1.8 2.3 2.8 3.9
      (260) 0.13 0.14 0.17 0.13 0.23 0.26 0.33 0.40 0.56
      1000 1.2 1.3 1.5 1.14 1.9 2.0 2.4 2.9 4.1
      (538) 0.17 0.19 0.22 0.16 0.27 0.29 0.35 0.42 0.59
      1500 1.5 1.6 1.7 1.39 2.2 2.1 2.6 3.1 4.2
      (816) 0.22 0.23 0.25  0.2 0.32 0.30 0.37 0.45 0.61
      2000 1.7 1.8 2.0 1.64 2.6 2.3 2.7 3.3 4.3
      (1093) 0.24 0.26 0.29 0.24 0.37 0.33 0.39 0.48 0.62
     To convert Btu-in/ft², hr, °F to Kcal-m², hr, °C,
multiply by 0.124.
Chemical Analysis
    Alumina – Al2O3 39.4 39.4 39.4 38 47.0 60.4 67.0 69.9 78.3
    Silica – SiO2 51.7 51.7 51.7 45 49.2 36.1 30.5 28.1 20.7
    Ferric Oxide – Fe2O3 0.6 0.6 0.6 0.3 0.6 0.4 0.3 0.3 0.2
    Titanium Oxide – TiO2 1.5 1.5 1.5 1.6 1.3 1.0 0.9 1.2 0.5
    Calcium Oxide – CaO 6.4 6.4 6.4 15 0.3 0.1 0.3 0.2 0.1
    Magnesium Oxide – MgO 0.1 0.1 0.1 0.1 0.1 0.2 0.0 0.1 0.1
    Alkalies, as Na2O & K2O 0.4 0.4 0.4 0.5 1.5 1.8 1.0 0.2 0.1