Marinite M
Marinite M Fireproof Marine Joiner Panels are lightweight, non-asbestos 4'x 8' sheets designed to provide structural strength and high thermal and acoustical insulating values in a variety of interior marine applications. Formed from calcium silicate with inert fillers and reinforcing agents, Marinite M panels are easily handled and cut to required shapes and sizes.
In addition to high strength and insulating values, Marinite M panels combine ease or erection, fire safety, durability, attractive appearance, and low maintenance for use as bulkheads, linings or ceiling material for new construction and reconversion of passenger vessels, cargo ships, tankers, drill rigs and platforms, plus for new construction and reconversion of U.S.C.G. and Navy vessels.
For greater design flexibility; Marinite M panels can be faced with a variety of decorative finishes including sheet metals and hard or soft plastic laminates. The panels provide an excellent base for melamine veneers, often preferred for their appearance and damage resistance.
| Dimensions |
|
Available Thicknesses |
½-2" |
| Sheet Sizes |
These sheets are 4' x 8' |
| Density |
| pcf |
46 |
| kg/cm² m3 |
737 |
| Modulus of Rupture |
| psi |
800 |
| kg/cm² |
56 |
| Compressive Strength |
| Ultimate load: psi |
- |
| Ultimate load: kg/cm² |
- |
| @ 5% Deformation: psi |
1000 |
| @ 5% Deformation: kg/cm² |
70 |
| Moisture |
| Normal % of dry wt |
3.0 |
| Thermal Conductivity (Mean Temperature, Btu-in/ft2, hr, °F ) |
| 400°F |
0.81 |
| 600°F |
0.79 |
| 800°F |
0.81 |
| 1000°F |
0.86 |
| Thermal Conductivity Mean Temperature, W/m°K |
| 204°C |
0.12 |
| 316°C |
0.11 |
| 427°C |
0.12 |
| 538°C |
0.12 |
| Shrinkage %: 24 hrs @ 1200°F |
| Length/width |
0.4 |
| Thickness |
1.4 |
| Electrical |
| Volume Resistivity, ohm-cm ASTM D 257 |
9.8x107 |
| Dielectric Strength, v/mil ASTM D495 |
45 |
| Screw Holding Strength @ 7/8" penetration |
| lbs |
200 |
| kg |
91 |
The physical and chemical properties of BNZ's materials represent values obtained in accordance with accepted test methods and are subject to normal manufacturing variations. They are supplied as a technical service and are subject to change without notice. Results should not be used for specification purposes.
Marinite M