MARINITE I Marinite I structural insulation is a non-asbestos incombustible material manufactured in 4'x8' panel form. These boards are designed to combine structural strength and high thermal insulating values in a variety of fireproofing and heat processing equipment applications. Formed from calcium silicate with inert fillers and reinforcing agents, Marinite I panels provide structure and insulation in a single, easily erected material. In addition to high strength and excellent thermal insulting characteristics, Marinite I structural insulation is highly damage-resistant, non-corroding, and extremely water-resistant. Marinite panels also provide fire safety, uniform temperature control, minimal maintenance, and fast, easy fabrication. PDF Data Sheet MSDS for MARINITE I
	CS85 \| Marinite a, c \| marinite P \| marinite m \| transite ht \| transite 1000

Marinite I Properties

Dimensions
Available Thicknesses	½-2"
Sheet Sizes	These sheets are 4' x 8'
Density
pcf	46
kg/ m³	737
Modulus of Rupture
psi	800
kg/cm²	56
Compressive Strength
Ultimate load: psi	-
Ultimate load: kg/cm²	-
@ 5% Deformation: psi	1000
@ 5% Deformation: kg/cm²	70

Moisture
Normal % of dry wt	3.0
Thermal Conductivity (Mean Temperature, Btu-in/ft², hr, °F )
400°F	0.81
600°F	0.79
800°F	0.81
1000°F	0.86
Thermal Conductivity Mean Temperature, W/m°K
204°C	0.12
316°C	0.11
427°C	0.12
538°C	0.12
Shrinkage %: 24 hrs @ 1200°F
Length/width	0.4
Thickness	1.4
Electrical
Volume Resistivity, ohm-cm ASTM D 257	9.8x10⁷
Dielectric Strength, v/mil ASTM D495	45
Screw Holding Strength @ 7/8" penetration
lbs	200
kg	91

The physical and chemical properties of BNZ's materials represent values obtained in accordance with accepted test methods and are subject to normal manufacturing variations. They are supplied as a technical service and are subject to change without notice. Results should not be used for specification purposes.